While you can purchase a piece of plastic from many different suppliers, there are some significant differences between these suppliers. Some of the main differences are in the manufacturers and the materials that you get supplied.
We see a wide range of materials and some drastically inferior grades of materials being sold to clients. Some materials have been produced too quickly or cooled too quickly causing a very high stressed plastic piece. These high stressed materials will warp, twist or crack when they get heated or during cutting. This material on the right is a piece of highly stressed Nylon. While cutting the material, our new customer had to stop the saw due to the severe warping and binding of the saw by this material. This new client brought this 24″ long part, and asked if we would cut it for him. We bought this part from him as an excellent example of a high stress plastic. (We did cut a quality piece of material to solve his problem).
One example of differences between manufacturers, is Gehr PVC rod is NSF 51 certified, while Simona PVC rod is not.
Other things you should consider when choosing a quality plastic supplier:
Quality of Materials
Origin of Materials
Huge In Stock Inventory of Plastic Rod
Expert Support
In Stock Materials
Cutting – Converting Services
Longevity – How Long Have They Been In Business (We started in 1975)
Product Knowledge and Experience Equals Quality Plastic Suppliers
We believe that providing quality products is only part of our duty to you. You have intrusted us to help with your requirements, and we believe we should be good stewards of this trust, all part of being a quality plastic supplier. A plastic sheet supplier should advise you if the material you are looking for is the ‘wrong’ material. Acrylic does not do well at 450 degrees. Styrene does not make a good chemical tank. HDPE and PTFE do not bond. These and many more ‘land mines’ are things we help our clients with everyday. We have an experienced client support team (plastic experts), and we value the opportunity to assist our clients with this experience. Go ahead, ask us a question – that is why we have a “Ask A Plasticologist” page on our website.
If you need help, from what are the properties of Acetal, to temperature range on Ultem, please contact us.We look forward to assisting you and all our clients. Feel free to contact us with any questions, concerns or requests – call us at 866-832-9315 or e-mail us here.
You know how bad it is when you get stressed out, with all the day to day challenges and issues? Well, plastics get stressed too.
The process of producing plastics into sheet, rod and tube is a stressful manufacturing process.
Stress free plastic manufacturing
The process to make a plastic sheet, plastic rod or plastic tube requires the plastic resin to be heated to temperatures of 350° – 500º to get the resin to flow through the machines.
The material is then pushed through a die at high pressure.
This heat and pressure cause many stresses to affect the plastic material.
The cooling of the plastic shape is critical
If the plastic cools to quickly, the surface cools and the center is still very hot, this is a major cause of internal stress.
Processed to quickly and voids or cold spots cause poor quality sections.
Processed to slowly and materials burn in the die and visible burn spots appear on the surfaces – bad material
Proper speed provides homogeneous material that has cooled at a uniform rate through the sheet yields a very low stress sheet
The stresses from this production can be very significant and can ruin your parts. One common prevention method is to anneal or stress relieve the raw material prior to machining, and may require stress relieving during machining if large amounts of material are being removed. The stress relieving process is a slow heat and cool process, contact us for details on your material or project.
Here is an example of a highly stressed plastic sheet, it is 1.250″ thick glass filled nylon sheet. The manufacturer sent us this sample to show the ‘quality’ of their material. We attempted to cut off a strip to do some testing, and you can see the results. This material warped so much it stopped our saw! We never did buy anything from this supplier.
Compression Molded Plastic Sheet and Brownies…
Nylon with huge amount of stress, cooled too quickly.
Yes, you read that right, brownies. I still remember the wonderful smell of my Grandma’s house when she was baking her special 2″ thick brownies. The smell was great, but I also remember the critical timing in the oven. She would open the oven and peek in, and close it quickly so as not to let the heat out. Then, when they looked about right she would open the oven and slip a toothpick into the center of the pan and pull it out again slowly. I can remember asking, “Grandma, why do you put in the toothpick into the brownie?”. The answer was, that the outside cooks quicker than the inside, and it takes a while to get the brownies to cook all the way to the center.Then, when they were all cooked, I would have to wait while they cooled. And, sometimes, if I didn’t wait quite long enough, when I would take a bit the center would burn my tongue. Ouch!
The interesting thing is, that plastics are about the same. Most plastics have a very low co-efficient of thermal conductivity (that is sure a mouth-full), which means that heat and cold don’t travel through the plastics well. This means that it takes a while to ‘cook’ the plastic all the way through, and not just the surfaces. And, just like my brownie story, the plastics take a long time to cool. If the outside of the plastic cools much faster than the inside, then large amounts of stress develop.
The process of compression molding of the plastic sheets is ideal for eliminating stress. The sheets cook slowly, so the entire sheet, including the center, is heated to a uniform temperature. The temperature is held at temperature to insure a fully cooked sheet (you can’t use a toothpick here). Then, over several hours, the temperature of the sheet and the entire compression molding press is lowered very s-l-o-w-l-y. This allows the center of the sheet to cool at the same rate as the external surfaces, and this yields a very stress free sheet. The premier manufacturer of this high quality compression molded sheet is Westlake Plastics. We have been a master supplier of the Westlake Plastic materials for over 35 years.
What should you do to eliminate stress?
If you are experiencing problems with your plastic materials, such as twisting, warping, ‘potato chipping’ or any other sign of stress, contact us. It is probably not your fault. There are dozens of manufacturers that produce engineering and mechanical plastic shapes, they are not all the same. During the production of materials, the process should include a secondary annealing step to remove stress from the newly product. By removing all stress from the sheet or rod you are insured of a ‘clean slat’ before you start machining or finishing. We only provide materials from top rated manufacturers, we truly care about the materials you receive from us.
If you have been experiencing problems with the materials you are getting from other suppliers, let us know, we can help eliminate your stress problems. E-mail us or call us at: 866-832-9315
We use cookies to ensure that we give you the best experience on our website. If you continue to use this site we will assume that you are happy with it.OkPrivacy policy